【Description】
2408 is a highly reactive functional groups of the amino silicone micro emulsion, specifically recommended for cotton, polyester fiber and cotton soft and lubricants.

【Properties】
Appearance: Pale yellow emulsion Ion: Cation
PH value :5.0-6 .5
Total solid content: 10 ± 2%
Volatile solvents: no dilution: water

Product Features
Given smooth soft feel of textiles, fine drape and crease recovery to improve the elasticity of textiles, soft washable and efficient impregnation and dyeing method can be applied, with most organic softener and textile auxiliaries compatibility, good dilution was excellent shear stability, anti-dielectric stability and resistance to hard water, has a good effect of increasing depth.
PH value in a wide range of stability, freeze / thaw cycles and stability has a good effect of deepening

Recommended Dosage】 【Reference
Impregnation method:
Recommended by fabric weight of 0.2% -2.0% silicone solids applied to the textiles, the best dosage will depend on the textile and organizational structure, and determined by the user. After rolling the fabric> 80 ℃ temperature drying, however, the proposed temperature is below 180 ℃, full effect of the fabric soft and adjusted to perfection.
Padding:
2408 new fabric softening agents can cause shear resistance suitable for dyeing and finishing equipment in the standard imposed on the dip, including jet dyeing equipment. Usage, proposed reference to the above drying conditions, the conditions of padding, dipping bath PH3.0-5.5 and temperature 45-50 ℃ exhaustion can give the best rate.
Dip switch and the conditions recommended astringent bath stains: dilution, the temperature should not exceed 60 ℃, PH value should be kept in the 3.0-8.5 range.
Alternate solution diluted stored at room temperature should not exceed 72 hours.
Although the vast majority of organic softeners and other textile finishing agent stability, and prior to this particular user prior to use in testing large-scale production in the finishing bath with the compatibility of components.